前言：PA6德国朗盛,BKV140H2.0 ,900051,尼龙原料,Durethan PA6
PA6德国朗盛BKV140H2.0 900051填料玻纤40%尼龙原料-宣传视频
PA6德国朗盛BKV140H2.0 900051填料玻纤40%尼龙原料物性表物性性能测试条件测试方法测试结果单位密度ASTM D792/ISO 11831.46物理性能测试条件测试方法测试结果单位收缩率TD:280°C,2.00mm2ISO294-40.75%TD:120°C,2hr,2.00mm3ISO294-40.090%MD:280°C,2.00mm2ISO294-40.21%MD:120°C,2hr,2.00mm3ISO294-40.070%机械性能测试条件测试方法测试结果单位拉伸模量23°CISO527-2/112000Mpa拉伸应力断裂,23°CISO527-2/5185Mpa拉伸应变断裂,23°CISO527-2/53.4%弯曲模量423°CISO178/A11000Mpa弯曲应力43.5%StrainISO178/A280Mpa23°CISO178290MpaFlexuralStrainatFlexuralStrength5(23°C)4.2%拉伸模量ASTM D638/ISO 52711200kg/cm?(MPa)[Lb/in?]拉伸强度ASTM D638/ISO 527174kg/cm?(MPa)[Lb/in?]弯曲模量ASTM D790/ISO 17810400kg/cm?(MPa)[Lb/in?]弯曲强度ASTM D790/ISO 178280kg/cm?(MPa)[Lb/in?]热性能测试条件测试方法测试结果单位燃烧性（率）UL94HB维卡软化点ASTM D1525/ISO R306200℃（℉）熔融温度5ISO11357-3220°C热变形温度0.45MPa,未退火ISO75-2/B217°C1.8MPa,未退火ISO75-2/A201°C冲击性能测试条件测试方法测试结果单位简支梁无缺口冲击强度-30°CISO179/1eU100kJ/m?23°CISO179/1eU110kJ/m?无缺口伊佐德冲击强度-30°CISO180/1U90kJ/m?23°CISO180/1U90kJ/m?23°CISO180/1A11kJ/m?-30°CISO179/1eA10kJ/m?23°CISO179/1eA15kJ/m?补充信息测试条件测试方法测试结果单位ISOShortnameISO1874PA6HI,GR,14-120,GF40